Wrought Superalloy GH3030 alloy

Wrought Superalloy

GH3030 alloy   

   

1.80Ni-20Cr Solid-solution strengthened high temperature alloy has simple chemical composition. 

It has good anti-oxidation, heat resistant, cold pressing and welding capability. It can work under 

800℃ normally 

with stable organization. It becomes single-phrase austenitic after solid-solution and can bear large stress for long time under high temperature.

 

2.Grade

GB:   GH3030(GH30)

TOCT: XH78T

 

3.

Chemical component

C	Si	Mn	P	S	Cr	Ni	Al	Ti	Fe
≤0.12	≤ 0.80	≤ 0.70	≤ 0.030	≤ 0.020	19.00- 22.00	balance	≤ 0.15	0.15- 0.35	≤ 1.50

4.Mechanical property

yield strength ó 0.2/MPa	tensile strength ó b/MPa	Elongation δ5%
320	635	35

5.Physics capability

density：8.4g/cm3      melting point：1374-1420℃

6.Application 

Mainly used in the firebox part under 800℃ of turbine engine and other high temperature parts under 

1100℃ with.

Making the high temperature parts of aviation and spaceflight engine.

The high temperature material of industrial wheel, energy, chemical and so on.

 

Please feel free to contact me at my email vivian (at) baoyuansteel (dot) com if you need above material.

Best regards

Vivian Zheng

Sales 

Shanghai Baoyuan Metal Materials Co.,Ltd

Add: No .188 ,Xinchun Road, Shanghai, China 201109

Tel: 0086 021 54192998-612

Fax: 0086 021 54192997

Website: http://www.baoyuansteel.com

vivian(at)baoyuansteel(dot)com

zhenghan1314(at)hotmail(dot)com

Skype:vivianzheng1314